Effect of sintering temperature on the leakage current of polycrystalline multiferrioc DyFeO3 material is reported. Samples were synthesized through Sol-Gel route. From the Rietveld refinement of X-Ray Diffraction (XRD) data it is observed that, samples were found to be of single phase. From the room temperature leakage current density study, it was observed that leakage current density decreases with increase of sintering temperature and Space charge limited conduction (SCLC) and Ohmic conduction mechanisms are dominant at lower and higher electric field values. The observations are corroborated in terms of microstructure changes with sintering temperature.
KEYWORDS:
Acknowledgments
SSKR is thankful to UGC and DST of Govt. of India for providing Junior Research Fellowship (JRF) under BSR-RFSMS and PURSE programme, respectively. Authors are also thankful to Dr. V. Ganesan, Centre Director, Prof. Ajay Gupta, Former Center Director, Dr. Mukul Gupta of UGC DAE CSR, Indore for providing experimental facilities and support.