Abstract
The effect of organomodified nanoclay on the morphology and properties of a (70/30 w/w) nylon 6/poly(methyl methacrylate) (PMMA) blend prepared by a melt processing method was investigated. The number average domain diameter (Dn ) of the dispersed PMMA phase was found to decrease with the addition of a small amount [0.5 per hundred resin (phr)] of clay in the blend. A much finer dispersion of the minor phase in the presence of a higher amount (5 phr) of clay indicated better mixing efficiency and improved morphology in the blend. X-ray diffraction indicated the exfoliation of the clays in the nylon 6 matrix, whereas PMMA chains only intercalated into the clay layers. However, the same effect of the clay was not observed in a (30/70 w/w) nylon 6/PMMA blend when nylon 6 became the dispersed domains. In the (30/70 w/w) nylon 6/PMMA blend, the addition of organomodified nanoclay (up to 2 phr) increased the Dn of the nylon 6 domains by preferential location of the clays inside the nylon 6 domains. Addition of styrene-maleic anhydride (SMA) copolymer effectively reduced the Dn of disperse phases in both compositions of the nylon 6/PMMA blends. Thus, in nylon 6/PMMA blends, clay platelets could prevent the coalescence of dispersed domains during melt mixing as long as it was dispersed in the matrix phase of the blend. Mechanical properties and thermal stability of the blends were also improved in the presence of clay.
Acknowledgment
The financial support from the Department of Science and Technology (DST), India, is highly acknowledged.