Abstract
Sodium 2,2’-methylene-bis (4,6-di-tert-butylphenyl) phosphate (commercial name: Irgastab NA-11) and N,N’-dicyclohexylnaphthalene-2,6-dicarboxamide (commercial name: NU-100) are highly effective nucleating agents for α-isotactic polypropylene (iPP) and β-isotactic polypropylene (iPP) respectively. Effects of a total concentration of 0.2 wt% NA-11/NU-100 compound nucleating agents with different ratios of NU-100 on mechanical properties and crystallization behaviors of iPP were studied in this paper. The results showed that good balance between decreased stiffness and increased toughness of iPP was realized when the ratio of NU-100 was 50 wt%. Compared with those of virgin iPP, tensile strength, tensile modulus, flexural strength, and flexural modulus of iPP nucleated by the compound nucleating agent with 50 wt% NU-100 decreased by only 2.9%, 4.8%, 3.8% and 6.1% respectively, while the notched Izod impact strength of the nucleated iPP was increased by 212.8%. In addition, differential scanning calorimetry analysis results showed that addition of the NA-11/NU-100 compound nucleating agent increased the peak crystallization temperature of iPP significantly, but the crystallization rate of the nucleated iPP decreased with increasing ratio of NU-100 in compound nucleating agents.
Acknowledgments
This work was financially supported by the Scientific Research Fund of Hunan Provincial Education Department under Grant No. 10B004, the Open Research Fund of Key Laboratory for Green Chemical Process of Ministry of Education, Wuhan Institute of Technology under Grant No. GCP 2011005, the Hunan Provincial Key Laboratory of Materials Protection for Electric Power and Transportation (No. 2012CL01), Changsha University of Science & Technology, and the P. R. China and the National Natural Science Foundation of China (No. 21001017).