Abstract
In this study, the NiFe2O4 nanoparticles have been prepared by co-precipitation and calcination process. Using a vibrating sample magnetometer (VSM), transmission electron microscopy (TEM), X-ray diffraction (XRD), energy dispersive spectrometer of X-ray (EDX), and X-ray photoelectron spectroscopy (XPS), the samples obtained by co-precipitation and then by further calcination have been analyzed. The experimental results show that the precursor synthesized by co-precipitation is the composite of both amorphous FeOOH and Ni(OH)2, but has no amorphous NiFe2O4. The results of both EDX and XPS revealed that the FeOOH species is wrapped up by Ni(OH)2 species. In the calcination process, the amorphous composite is dehydrated and transformed gradually into crystalline NiFe2O4 nanoparticles, with the metal ions diffusing. The reaction is different from the one used to prepare other ferrite (e.g., CoFe2O4, MnFe2O4, Fe3O4, etc.) nanoparticles directly by co-precipitation. With increasing calcination temperature, the NiFe2O4 grains grow and the magnetization is enhanced.
Keywords:
Acknowledgements
Financial support for this study was provided by the National Natural Science Foundation, P.R. China (No. 11074205) and by Natural Science Foundation Project of CQ CSTC.