Glass formation in the system Li2B4O7–Pb3O4–CuO using X-ray diffraction

, &
Pages 475-488 | Received 11 Jul 2014, Accepted 01 Nov 2014, Published online: 17 Feb 2015
 

Abstract

X-ray diffraction was performed to construct the phase diagram for the ternary Li2B4O7–Pb3O4–CuO glass system. Three principal regions were identified: (1) a glass-forming region observed at the composition (75 < Li2B4O7 < 100) mol%, (0 < CuO < 35) mol% and (0 < Pb3O4 < 70) mol% in the ternary system, and (100 − x) mol% Li2B4O7x mol% Pb3O4 where x = 0 up to 70, (100 − y) mol% Li2B4O7y mol% CuO where y = 0 up to 25 in the binary system;. (2) a crystalline region: all compositions prepared from the binary system Pb3O4–CuO and the ternary system containing Li2B4O7 up to 60 mol%; (3) a partially crystalline region formed between the glass and crystalline regions.

Log in via your institution

Log in to Taylor & Francis Online

PDF download + Online access

  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 61.00 Add to cart

Issue Purchase

  • 30 days online access to complete issue
  • Article PDFs can be downloaded
  • Article PDFs can be printed
USD 1,144.00 Add to cart

* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.