Transport and Deposition of Alumina Nanoparticles in Water Saturated Porous Media: An Experimental Study

Abstract

Transport and deposition of nanoparticles (NPs) have drawn great attention in different fields of engineering in recent years because of their potential risk to the environment. In this study, mobility of aluminum oxide NP, one of the most popular metal oxide NPs, was studied in synthetic saturated porous media. The impacts of ionic strength using monovalent (NaCl) and divalent (MgCl₂) salt solution, pH, and NPs concentrations on nano-alumina mobility were investigated. The experimental results showed that the transport of nano-alumina was influenced by ionic strength; the highest mobility was observed at the 0.01 M solution and decreased by increasing ionic strength. Moreover, the suspension containing alumina NPs presented the best mobility behavior in the acidic solution (pH = 2) in comparison with neutral and basic solutions. Consequently, transport of NPs with particle size distribution lower than 100 nm through porous media was facilitated at the acidic, low ionic strength condition. In addition, faster elution occurred when the influent concentration was increased from 0.1 wt% to 0.3 wt%. Finally, it is expected that ionic strength, pH of solution, and NPs concentration will be key parameters to control the nano-alumina mobility.

Keywords:

• Alumina nanoparticles
• deposition
• porous media
• transport behavior

Notes

Color versions of one or more of the figures in the article can be found online at www.tandfonline.com/ldis.