Chitosan films incorporated with nettle (Urtica Dioica L.) extract-loaded nanoliposomes: II. Antioxidant activity and release properties

, , , &
Pages 449-459 | Received 30 Dec 2015, Accepted 28 Jun 2016, Published online: 14 Jul 2016
 

Abstract

Chitosan films were loaded with NE nettle (Urtica dioica L.) extract (NE) at concentrations of 0, 0.5, 1 and 1.5%w/w in the free or nanoliposomal form to obtain active and nanoactive films, respectively. The antioxidant potential of the films containing NE-loaded nanoliposomes was decreased in comparison of free NE incorporated films. Diffusion of NE to soybean oil was enough to delay the induction of the oxidation of soybean oil stored for 60 days in contact with chitosan based films. Release studies indicated that the release rate of NE in 95% ethanol simulant significantly decreased by the nanoencapsulation of NE. The diffusion coefficient (D) for chitosan films containing 1.5%w/w of free and encapsulated NE at 25 °C was 18.80 and 3.68 × 10−7 cm2 s−1, respectively. Moreover, the formation of nanoliposomes diminished the increasing effect of temperature on the release rate as when storage temperature increased from 4 °C to 40 °C.

Disclosure statement

The authors report no declarations of interest.

Log in via your institution

Log in to Taylor & Francis Online

PDF download + Online access

  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 65.00 Add to cart

Issue Purchase

  • 30 days online access to complete issue
  • Article PDFs can be downloaded
  • Article PDFs can be printed
USD 721.00 Add to cart

* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.