ABSTRACT
This paper investigates the effect of post-deposition heat treatment on porosity, microstructure, and mechanical properties of Ti–6Al–4V produced via an Electron Beam Melting process. Samples were studied in the conditions of as-built and heat treated at 920°C and 1030°C. The as-built samples were characterised by columnar β grains consists of α+β microstructure with Widmanstätten and colony morphologies were found. Heat treatment resulted in increased α lath width. The yield strength and ultimate tensile strength was greater in the as-built condition than wrought material. Porosity re-growth occurred after heat treatment but it did not affect the tensile properties. Greater ductility after heat treatment was attributed to the larger α lath width which increases effective slip length.