Grain growth in IN718 superalloy fabricated by laser additive manufacturing

ABSTRACT

The grain growth mechanism of IN718 superalloy fabricated by selective laser melting (SLM) was studied. Epitaxial growth with the same crystallographic orientation or rotating by 90° across the melting pool boundary and competitive growth in the same melting pool were observed. Either of the two patterns of epitaxial growth can maintain the same grain across the melting pool boundary. Competitive growth is determined by both the heat flow direction and preferred crystallographic orientation. In SLM, the grains grow along the preferred crystallographic orientation owing to a high solidification rate. The smaller the deviation angles between the heat flow direction and the preferred crystallographic orientation, the faster the grain growth rate.

KEYWORDS:

• Epitaxial growth
• crystallographic orientation
• IN718
• competitive growth
• selective laser melting

Acknowledgement

This study was supported by National Natural Science Foundation of China (No.11672140) and (No.11762014) and Hulunbiur College (No. 2019FDYB05).

Disclosure statement

No potential conflict of interest was reported by the author(s).

Additional information

Funding

This study was supported by National Natural Science Foundation of China (Grant Number 11672140) and (Grant Number 11762014) and Hulunbiur College (Grant Number 2019FDYB05).