Abstract
In the present study, strength variations across the type 316LN stainless steel weld joints processed by advanced hot wire tungsten inert gas, activated tungsten inert gas, and hybrid laser metal inert gas welding processes were evaluated using automated ball indentation technique. The secondary dendrite arm spacing (SDAS) associated with welding heat input and welding thermal cycles strongly influenced the strength properties across the weld joints. The strength properties were lower at 823 K compared to 298 K because of thermally activated deformations. The hybrid laser metal inert gas welding process exhibited significantly narrower weld and higher strength in the weld and heat-affected zone due to finer SDAS and grain size, respectively, than the other weld joints.
Acknowledgements
The authors acknowledge Mr Aashranth. B, MMG for SEM, Dr Arup Dasgupta, and Ms Vaishnavi Krupa, MMG, IGCAR for EBSD analysis. One of the authors, Mr Pavan A R, would like to thank DAE for the fellowship.
Disclosure statement
No potential conflict of interest was reported by the author(s).
Ethical approval
This paper is an original work and has been neither published nor submitted for publication elsewhere.
Data availability statement
Data are available on request from the authors.