Abstract
In this article, we report on the synthesis and thermotropic behaviour of methacrylic polymers containing 4′-(4-alkyloxyphenyl)azobenzene mesogens attached to the backbone through n-alkyloxy spacers of 6 or 10 methylene groups. Polymerisations were carried out via free radicals using azobisisobutyronitrile (AIBN) as initiator. Chemical structures of polymers and their precursors were characterised by 1H NMR spectroscopy. Thermogravimetric analysis showed that azopolymers are thermally stable up to temperatures around 300°C. The thermotropic liquid-crystalline (LC) behaviour was studied by differential scanning calorimetry (DSC), polarized optical microscopy (POM) and X-ray diffraction (XRD). Results indicate that all synthesised mesogens, monomers and polymers developed two or more orthogonal LC phases in wide temperature ranges. Mesogens and monomers developed nematic and smectic phases, whereas polymers exhibited only smectic phase. In polymers, the arrangement of mesogens depends on the relative length of the spacer and the terminal flexible chain; two distinct structural models were proposed based on chemical interactions and steric constrains. The trans–cis photoisomerisation of monomers and polymers in solution was also studied. High cis-isomer contents (>80%) were reached in relative short irradiation times despite the steric constrains imposed by the polymer backbone.
Acknowledgements
This work was supported by the CONACYT, México (Project 61773-R). Karla G. Gutiérrez acknowledges the grant received from CONACYT-México (ref. 211982). The authors thank Prof. D. Guillon and Dr. B. Heinrich from the IPCMS (Strasbourg, France) for the XRD facilities and G. Méndez and M. García from CIQA for their helpful technical assistance in the DSC and NMR experiments, respectively.