ABSTRACT
Polymer dispersed liquid crystal (PDLC) films have potential applications in many aspects due to unique electrically switching properties, and thus the films with excellent comprehensive properties are highly demanded at present. In this study, aromatic polyurethane acrylate (PUA) was used as polymer-matrix, and effect of diluents [lauryl methacrylate (LMA) and isobornyl acrylate (IBOA)] content on the electrical-optical properties of PDLC films was investigated. The results indicate that increase of PUA/LMA or decrease of LMA/IBOA weight ratio increases threshold and saturation voltages (Vth and Vsat), decreases on- and off-state transmittances (Ton and Toff) and increases contrast ratio. Under optimised PUA/LMA weight ratio of 31/19 or PUA/LMA/IBOA weight ratio of 31/15/4, the Vth and Vsat of the films first increase and then decrease with increasing Ag nanowires (NWs) content, and better overall properties are achieved at 0.05 or 0.075 wt.% Ag NWs, respectively. In order to explore essential reasons for the influence of diluents and Ag NWs on the properties of PDLC films, the relationships between film properties (Vth or Vsat, Ton, Toff, and response time) and liquid crystal (LC) droplets size were analysed emphatically, and the changes of system viscosity and anchoring force between polymer-matrix and LC droplets were also discussed.
GRAPHICAL ABSTRACT
Acknowledgments
This work was supported by the Opening Project of State Key Laboratory of Materials Processing and Die & Mould Technology (P2014-06).
Disclosure statement
No potential conflict of interest was reported by the authors.
Supplemental data
Supplemental data for this article can be accessed online at https://doi.org/10.1080/02678292.2023.2182924