Powder Deposition in Three Parallel-Oriented Dies of Different Shapes

Abstract

Uniformity of bulk density distribution during the die filling process is required to minimize quality problems, such as distortion and cracking, for powder compacts. Understanding the die filling process is necessary in ensuring a uniform powder deposition. The second-generation pressure deposition tester (PDT-II) was used to investigate the deposition process and final pressure distribution of powder filling in toroidal, cylindrical, and E-shaped dies. All tests were conducted using a spray-dried free-flowing granular powder. The results indicated that for toroidal dies: (1) the area around 0° orientation (the leeward end) had the highest pressure values (1186.7 to 2498.0 Pa), with the average pressure values of the remaining area 353.7–648.0 Pa; (2) the pressure distribution was symmetrical about the centerline parallel to the feed shoe movement direction; (3) the highest feed shoe speed (500 mm/s) led to the most nonuniform pressure distribution among the three speeds; (4) higher feed shoe speed did not always result in higher final pressure values; and (5) the right die tended to have higher final pressure values (215.0 to 2498.0 Pa) than the center die (95.4 to 2052.5 Pa). For E-shaped dies: (1) the final pressure values of the middle leg (308.9 to 760.7 Pa) were higher than those of the left and the right legs (148.9 to 530.3 Pa); (2) the area along the backside had the highest final pressure value (1054.6 to 1303.8 Pa); (3) the pressure distribution was symmetrical about the centerline parallel to the feed shoe movement direction; and (4) neither the center die nor the right die always had higher pressure values than the other one at all locations. Comparison between cylindrical and toroidal dies indicated that: (1) neither of the two die shapes (cylinder and toroid) led to consistently higher or lower final pressure values at all locations and (2) for all three feed shoe speeds, the toroidal die had higher average final pressure values in the 0° orientation.

Keywords:

• cylindrical dies
• E-shaped dies
• feed shoe speed
• PDT-II
• powder deposition into dies
• pressure deposition tester
• toroidal dies
• uniformity of pressure distribution

The authors thank the Particulate Materials Center at Penn State University and the Pennsylvania Agricultural Experiment Station for providing funding for this project.