Abstract
Nalita (Trema orientalis) is one of the fastest growing trees in the tropical countries. The structural characteristics of lignin isolated at different ages of Nalita wood (Trema orientalis) by acidolytic dioxane method were examined by UV, FTIR, 1H‐NMR and 13C‐NMR spectroscopy, alkaline nitrobenzene oxidation, molecular weight determination, elemental and methoxyl analysis. The data were compared with aspen lignin. The structural analysis revealed that Nalita wood lignin is syringyl‐guaiacyl type. The methoxyl content in Nalita wood lignin was lower than aspen lignin. The C9 formulas for 30‐months‐old Nalita was C9H9.31O3.13(OCH3)1.27, whereas that of aspen was C9H8.94O3.15(OCH3)1.47. The weight average molecular weight of Nalita wood lignin was decreased from 36,500 to 25,500 with increasing tree age from 12 to 30 months, whereas weight average molecular weight of aspen was 20,000. Both alcoholic and phenolic hydroxyl group in Nalita wood lignin is lower than aspen lignin.
The authors thank the authority of Chonbuk National University for providing financial support from the postdoctoral fund to carry out this research. The authors are also grateful to Dr. Fujita for carrying out elemental analysis.