Facile synthesis of Fe₃O₄/MoS₂ nanohybrid for solid phase extraction of Ag(I) and Pb(II): kinetic, isotherm and thermodynamic studies

ABSTRACT

Recently, MoS₂ with abundant electron density in its structure attracted more attention as an adsorbent for environmental remediation. However, hard manipulation of target solution owing to high dispersibility in aqueous media restricts its application as adsorbent. Preparation of Fe₃O₄/MoS₂ nanohybrid can solve this problem. Also, this nanohybrid improves adsorption capacities of target ions. In this work, Fe₃O₄ nanoparticles, MoS₂ nanosheets and hybrid of these two were synthesised and then characterised by X-ray diffraction, energy-dispersive X-ray spectroscopy, field emission scanning electron microscopy, transmission electron microscopy, Fourier transforms infrared spectra, Brunauer–Emmett–Teller surface area and vibrating sample magnetometer. Subsequently, adsorption of Ag(I) and Pb(II) ions from aqueous solution by these three adsorbents was examined in detail and compared with each other while the adsorption conditions including the pH value, contact time, dosage of sorbent, elution conditions and interfering ions have been optimised. According to obtained results, prepared nanohybrid showed enhanced adsorption capacities for both ions relative to naked Fe₃O₄ and MoS₂. The limits of detection for Ag(I) and Pb(II) were calculated as 0.49 µg L⁻¹ and 2.7 µg L⁻¹, respectively, and the relative standard deviation percentages (n = 5) for Ag(I) and Pb(II) were 2.8%, and 3.0%, respectively. Furthermore, the preconcentration factors were 300 and 75 for Ag(I) and Pb(II) ions, respectively. Moreover, kinetic studies showed that pseudo-second-order model can better describe target analytes adsorption properties by every three adsorbents. Regeneration of the adsorbents was performed with HCl/thiourea mixture.

KEYWORDS:

• Solid phase extraction
• flame atomic absorption spectrometry
• thermodynamic study: enhanced adsorption capacity

Acknowledgements

Support from the Reserach Council of the University of Tehran is gratefully acknowledged.

Disclosure statement

No potential conflict of interest was reported by the authors.

Supplemental data

Supplemental data for this article can be accessed here.

Additional information

Funding

Financial support from the Research Council of the University of Tehran is through Grant Number 94038 gratefully acknowledged.