Photocatalytic Degradation of the Herbicide Erioglaucine in the Presence of Nanosized Titanium Dioxide: Comparison and Modeling of Reaction Kinetics

The present work mainly deals with photocatalytic degradation of a herbicide, erioglaucine, in water in the presence of TiO₂ nanoparticles (Degussa P-25) under ultraviolet (UV) light illumination (30 W). The degradation rate of erioglaucine was not so high when the photolysis was carried out in the absence of TiO₂ and it was negligible in the absence of UV light. We have studied the influence of the basic photocatalytic parameters such as pH of the solution, amount of TiO₂, irradiation time and initial concentration of erioglaucine on the photodegradation efficiency of erioglaucine. A kinetic model is applied for the photocatalytic oxidation by the UV/TiO₂ system. Experimental results indicated that the photocatalytic degradation process could be explained in terms of the Langmuir–Hinshelwood kinetic model. The values of the adsorption equilibrium constant, K, and the second order kinetic rate constant, k, were 0.116 ppm^{− 1} and 0.984 ppm min^{− 1}, respectively. In this work, we also compared the reactivity between the commercial TiO₂ Degussa P-25 and a rutile TiO₂. The photocatalytic activities of both photocatalysts were tested using the herbicide solution. We have noticed that photodegradation efficiency was different between both of them. The higher photoactivity of Degussa P-25 compared to that of rutile TiO₂ for the photodegradation of erioglaucine may be due to higher hydroxyl content, higher surface area, nano-size and crystallinity of the Degussa P-25. Our results also showed that the UV/TiO₂ process with Degussa P-25 as photocatalyst was appropriate as the effective treatment method for removal of erioglaucine from a real wastewater. The electrical energy consumption per order of magnitude for photocatalytic degradation of erioglaucine was lower with Degussa P-25 than in the presence of rutile TiO₂.

Keywords:

• Erioglaucine
• Herbicides
• Photocatalysis
• Advanced oxidation process
• TiO₂

AKNOWLEDGEMENTS

The authors thank the university of Tabriz, Iran for financial and other supports.