Properties of Polypropylene (PP)/Ethylene-Propylene Diene Terpolymer (EPDM)/Natural Rubber (NR) Vulcanized Blends: The Effect of N,N-m-Phenylenebismaleimide (HVA-2) Addition

Abstract

This paper discusses process development, tensile properties, morphology, oil resistance, gel content, and thermal properties of polypropylene (PP)/ethylene-propylene diene terpolymer (EPDM)/natural rubber (NR) vulcanized blends with the addition of N,N-m-phenylenebismaleimide (HVA-2) as a compatibilizer. Blends were prepared in several blend ratios in a Haake Polydrive with temperature and rotor speed of 180°C and 50 rpm, respectively. Results indicated that the combination of dicumyl peroxide (Dicup) with HVA-2 shows high torque development and stabilization torque as compared to the blend with Dicup vulcanization alone. In terms of tensile properties, the combination of Dicup with HVA-2 shows higher tensile strength, tensile modulus (M₁₀₀), elongation at break, oil resistance, and gel content in all blend ratios compared to similar vulcanized blends with Dicup without HVA-2 addition. Scanning electron microscope (SEM) micrographs of the blends support that the cross-linking and compatibilization occur during the process of the vulcanized blend containing HVA-2. In the case of crystallinity of the blends, the addition of HVA-2 in Dicup vulcanized blend revealed a tendency for the percentage of crystallinity (Xc) to decrease. The addition of HVA-2 in Dicup vulcanization also produced blends with good thermal stability dealing with the so-called coagent bridge formation.

Keywords:

• Crystallinity
• Dicup
• EPDM
• HVA-2
• Natural rubber
• Polypropylene
• Thermal stability

Notes

^a Irganox 1010 (0.4 phr).

^b Based on the rubbers content (EPDM and NR).

^c Based on the NR content.