Abstract
Viscosity and peel strength of epoxidized natural rubber (ENR 25)-based adhesive was investigated in the presence of magnesium oxide. Petro resin and toluene were used as the tackifier and solvent, respectively. Viscosity was determined by a HAAKE Rotary Viscometer whereas peel strength was measured by a Lloyd Adhesion Tester. Results show that viscosity of adhesive increases with increasing magnesium oxide loading. However, for the peel strength, a maximum is obtained at 20 phr of magnesium oxide where maximum wettability and compatibility occurs. For a fixed filler concentration, peel strength increases with coating thickness for the three modes of peel tests.