Self-Cross-Linking Hydrogenated Nitrile-Butadiene Rubber Latex/Polyvinyl Chloride Emulsion Composite Film and Its Properties

Yang Han State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, People's Republic of China; Key Laboratory of Beijing City on Preparation and Processing of Novel Polymer Materials, Beijing University of Chemical Technology, Beijing, People's Republic of China
,
Lin Su State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, People's Republic of China; Key Laboratory of Beijing City on Preparation and Processing of Novel Polymer Materials, Beijing University of Chemical Technology, Beijing, People's Republic of China
,
Lixin Mao State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, People's Republic of China; Key Laboratory of Beijing City on Preparation and Processing of Novel Polymer Materials, Beijing University of Chemical Technology, Beijing, People's Republic of China
,
Liqun Zhang State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, People's Republic of China; Key Laboratory of Beijing City on Preparation and Processing of Novel Polymer Materials, Beijing University of Chemical Technology, Beijing, People's Republic of China
&
Dongmei Yue State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, People's Republic of China; Key Laboratory of Beijing City on Preparation and Processing of Novel Polymer Materials, Beijing University of Chemical Technology, Beijing, People's Republic of ChinaCorrespondence[email protected]
Pages 306-311 | Published online: 31 Jan 2014
 
Sample our Physical Sciences journals, sign in here to start your FREE access for 14 days

Abstract

A new type of self-cross-linking hydrogenated carboxylated nitrile-butadiene rubber (HXNBR)/polyvinyl chloride (PVC) composite film was prepared from their mixed emulsions. HXNBR latex was obtained by diimide hydrogenation. The HXNBR/PVC composite film can be self-cross-linked without any additional cross-linking agent. The properties of composite films, including film-forming property, morphology, physical properties, swelling behavior, and ageing properties were investigated. When PVC content was lower than 30%, the composite film showed no crack in the surface, especially at 20% of PVC content, the composite film showed excellent mechanical properties. The addition of 20% PVC improved thermal stability of HXNBR film.

Log in via your institution

Access through your institution

Log in to Taylor & Francis Online

Restore content access

Restore content access for purchases made as guest
Purchase options * Save for later

PDF download + Online access

  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 61.00 Add to cart

Issue Purchase

  • 30 days online access to complete issue
  • Article PDFs can be downloaded
  • Article PDFs can be printed
USD 687.00 Add to cart

* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.