Abstract
The effect of minor additions of barium oxide and titania on the formation of forsterite from pure raw materials and commercial grade raw materials was studied at 1450°C. It was observed that TiO2 was more effective than BaO in the formation of forsterite phase. The addition of 2–3 wt% of each additive produced an optimum value of density and dielectric constant of the forsterite ceramics.