Abstract
Ferrographic analysis was used to determine the types and quantities of wear particles generated during accelerated rolling contact fatigue tests. The NASA five-ball rolling contact fatigue tester was used. Ball specimens were made of AMS 5749, a corrosion resistant, high-temperature bearing steel. The lubricant was a super-refined naphthenic mineral oil. Conditions included a maximum Hertz stress of 5.52 × 109 Pa and a shaft speed of 10 000 rpm. Four types of wear particles were observed; normal rubbing wear particles, fatigue spall particles, spheres, and friction polymer.
Presented as an American Society of Lubrications Engineers paper at the ASLE/ASME Lubrication Conference in Kansas City, Missouri, October 3–5, 1977