Molecular dynamics simulations of performance degradation of cellulose nanofibers (CNFs) under hygrothermal environments

, , , , &
Pages 1172-1180 | Received 03 Dec 2019, Accepted 03 Aug 2020, Published online: 19 Aug 2020
 

ABSTRACT

Cellulose nanofibers (CNFs) have received wide attention in recent years. However, the performance degradation of CNFs has become a serious problem restricting their development when exposed to hygrothermal environments. While most studies have attributed the degradation behaviour to the water susceptibility of CNFs, the internal mechanism and detailed performance evolution are seldom reported at the molecular level. This paper used molecular dynamics simulation to study the effects of moisture on the diffusion, structure, mechanical strength, and chemical stability of CNFs. Simulation results indicated that the water diffusivity in amorphous cellulosewas10 times higher than in crystalline cellulose, demonstrating the preferential water uptake in amorphous cellulose. Meanwhile, the diffusion coefficient of water was found to be almost constant in the amorphous cellulose with less than 5% moisture. This behaviour was related to the amount and size of pores in amorphous cellulose. Furthermore, under high humidity, there was a significant decrease in mechanical strength and chemical stability of amorphous cellulose. However, in the range 0–5.0% of water absorption, the mechanical performance showed a slight increase, and chemical stability was also relatively high. These results provide a crucial point (<5 wt% moisture) for CNFs to remain stable under hygrothermal environments.

Disclosure statement

No potential conflict of interest was reported by the author(s).

Additional information

Funding

The authors acknowledge the National Key R&D Program of China [grant number 2017YFB0903801], the Science and Technology Project of SGCC [grant number SGTYHT/14-JS-188], National Science Foundation of China [grant number 51707016], the 111 Project of the Ministry of Education, China [grant number B08036], the Key Research and Development Program of Chongqing about Key Technological Innovation in Industries [grant number 1026223532180165] for supporting this research.

Log in via your institution

Log in to Taylor & Francis Online

PDF download + Online access

  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 61.00 Add to cart

Issue Purchase

  • 30 days online access to complete issue
  • Article PDFs can be downloaded
  • Article PDFs can be printed
USD 827.00 Add to cart

* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.