Abstract

A study of electrophysical and thermodynamic properties of C₆₀ single crystals under step shock loading has been carried out. The increase and the following reduction in specific electroconductivity of C₆₀ fullerite single crystals at step shock compression up to pressure 30 GPa have been measured. The equations of state for face centred cubic (fcc) C₆₀ fullerite as well as for two-dimensional polymer C₆₀ and for three-dimensional polymer C₆₀ (3D-C₆₀) were constructed. The pressure–temperature states of C₆₀ fullerite were calculated at step shock compression up to pressure 30 GPa and temperature 550 K. The X-ray diffraction studies of shock-recovered samples reveal a mixture of fcc C₆₀ and a X-ray amorphous component of fullerite C₆₀. The start of the formation of the X-ray amorphous component occurs at a pressure P _m≈ 19.8 GPa and a temperature T _m≈ 520 K. At pressures exceeding P _m and temperatures exceeding T _m, the shock compressed fullerite consist of a two-phase mixture of fcc C₆₀ fullerite and an X-ray amorphous component presumably consisting of the nucleators of polymer 3D-C₆₀ fullerite. The decrease in electroconductivity of fullerite can be explained by the percolation effect caused by the change of pressure, size and number of polymeric phase nuclei.

Keywords:

• High pressure
• Equation of state
• Conductivity
• Fullerenes
• Hugoniot

Acknowledgements

The authors thank M.G. Spirin for spectrophotometric metrology of C₆₀ solution. This work was carried out under financial support of the programme of the Presidium Russian Academy of Sciences ‘Investigations of matter under extreme conditions’.