Abstract
This work describes the influence of laser treatment on the structure and some properties of Al 2 O 3 , Al 2 O 3 + 5%Ni, Al 2 O 3 (95%Ni + 5%Al), Al 2 O 3 + 5%Ni - (95%Ni + 5%Al) and Al 2 O 3 + 5%Ni + CrAl layer oxide ceramic coatings of about 100 m thickness deposited by air plasma spraying on a heat-resistant alloy with a nickel matrix. It has been stated that laser remelting of power density 0.01-0.2 10 9 W m 2 and scanning rate within 5-7 m min 1 ensures good quality of ceramic coatings in comparison with not-remelted coatings. Laser treated ceramic coatings have a better thermal conductivity than as deposited layers. As shown by model calculations, after laser treatment, they show a smaller temperature drop over a given thickness. The erosion resistance of the coatings, however, is greater after laser treatment.