Fabrication and characterisation of an electrospun tubular 3D scaffold platform of poly(vinylidene fluoride-co-hexafluoropropylene) for small-diameter blood vessel application

Abstract

In this research, nanofibrous 3D tubular (~4-mm-diameter tube) scaffolds of poly (vinylidene fluoride-co-hexafluoropropylene) were fabricated by electrospinning. The role of surface charge in the success of these scaffolds for potential small-diameter artificial vascular grafts has been investigated using streaming potential study. Prior to endothelial cell culture, surface properties such as wettability and the surface charge of these tubular scaffolds were evaluated using unmodified and fibrinogen-adsorbed surfaces to understand their interaction with surrounding environment. The tubular scaffolds constructed using electrospinning show similar mechanical properties such as tensile strength and elastic modulus as those of native vessels. Whilst endothelial cell proliferation on unmodified tubes, as analysed by scanning electron microscopy, was found to be moderate, a simple process of dynamic fibrinogen adsorption was seen to enhance the endothelialisation of these tubular grafts. The high negative zeta potential values, high strength, robustness and structural reliability of the scaffolds represent them to be promising biomaterials for vascular graft applications.

Keywords:

• electrospinning
• SEM
• poly(vinylidene fluoride-co-hexafluoropropylene)
• fibres
• zeta potential
• platelets
• vascular graft

Acknowledgements

The authors are thankful to ARC for financial support of this work through ARC grants and to Sara Azari, Division of Information Technology, Engineering and the Environment, University of South Australia for their support in streaming potential analysis. One of the authors (FA) is thankful for the scholarship supported by NED University of Engineering & Technology Karachi, Pakistan.