Optimisation of hybridisation effect in graphene reinforced polymer nanocomposites

Abstract

This article focuses on the optimisation of electrical and mechanical properties of hybrid blends of polyoxymethylene (POM) as primary thermoplastic matrix, polypyrrole (PPY) as secondary conducting polymer and graphene (G) as reinforcement. An initial Taguchi analysis was performed with a focus on improving electrical conductivity (σ) and tensile strength. A mixture analysis using ‘simplex’ statistical design was applied to develop an experimental subset that identified an optimal combination in weight-percentage. Both electrical and mechanical properties were improved by the addition of PPY and graphene particles due to hybridisation mechanism as well as double percolation threshold. The maximum electrical conductivity of 0.95 S cm⁻¹ was achieved with POM reinforced with 3 wt.% of G and 2.5 wt.% of PPY loading. The mechanical properties were found to be increased with increase in addition of both G and PPY.

Keywords:

• hybridisation
• graphene composites
• electrical conductivity
• ultimate tensile strength
• statistical analysis
• morphology
• sub-set optimisation