Al-Ni-Ru alloys with a wide composition range have been synthesized and examined by X-ray and electron diffraction experiments. In this system, two types of decagonal (d) phases are formed, namely basic-type and superlattice-type d phases. Annealing experiments have shown that the basic-type d phase is stable at high temperatures and that its single-phase region is located in a small composition range around Al 75 Ni 15 Ru 10 . On the other hand, the superlattice-type d phase is metastable and has been found to form only in the samples before annealing. Besides the d phases, a high-order crystal approximant phase with lattice parameters a = 99.5 Å and b = 84.6 Å has been found. The structural relation between the approximant phase and the d phase is discussed in terms of a phason tensor.