Abstract
The role of the dynamic interactions between hydrogen in a solid solution and the stress-induced martensite transformation in hydrogen embrittlement has been investigated using trained Ni–Ti superelastic alloy. In a cyclic tensile test in the stress plateau region caused by stress-induced martensite and reverse transformations after hydrogen charging, a further decrease in the critical stress for the martensite transformation is observed. In addition, the number of cycles to fracture for a trained specimen is significantly larger than that for a non-trained specimen. Since most of the charged hydrogen is preferentially trapped in defects induced by training, the hydrogen embrittlement is considerably suppressed as a result of decreasing interactions between the hydrogen and the transformation. The present results indicate that hydrogen in a solid solution more strongly interacts with the stress-induced martensite transformation than hydrogen trapped in defects, thereby further enhancing the hydrogen embrittlement related to phase transformations.