ABSTRACT
In the present study, dissimilar weld joint was prepared using the P91 and P92 steel plate of 8-mm thickness, using the multi-pass gas tungsten arc (GTA) welding with filler (weld 1) and autogenous tungsten inert gas welding (A-TIG) process (weld 2). Evolution of δ-ferrite patches was studied in weld zone and heat affected zone (HAZ) for both weld 1 and weld 2. Effect of varying post weld heat treatment (PWHT) duration was also studied on δ-ferrite patches and mechanical properties of the dissimilar weld joint. PWHT was carried out at 760°C. For weld 2, weld zone showed poor impact toughness and higher peak hardness as compared to weld 1. After the PWHT, a considerable reduction in hardness was obtained for both weld 1 and weld 2,while impact toughness of weld zone showed a continuous increment with PWHT duration. For weldments characterisation, optical microscope, scanning electron microscope (SEM) and microhardness tester were utilised.
Disclosure statement
No potential conflict of interest was reported by the authors.