Corrosive Wear and Mechanical Properties of Ni/Al₂O₃ Micro- and Nanoparticulates-Reinforced Coatings on Ti-6Al-4V Alloy

Abstract

Nanocomposite coatings can endow a plated surface with various properties such as wear resistance, high-temperature corrosion protection, oxidation resistance, and self-lubrication. This work studies the corrosion and corrosive wear resistance of electroplated nickel nanocomposite coatings on Ti-6Al-4V alloy in a Hank's solution, adding various concentrations of an Al₂O₃ powder in plating solution, with particle diameters of 20–30 nm and 1 μm for comparisons. The experimental results showed that the content of Al₂O₃ incorporated into the electroplated nickel composite coating increased with the concentration of Al₂O₃ powder in the electroplating solution, and increasing the surface hardness, corrosion, and corrosive wear resistance of electroplated nickel micro- and nanocomposite coatings caused smearing of the nodule boundary and elimination of voids in the deposits. The Al₂O₃ nanoparticulates were embedded and distributed more uniformly than the Al₂O₃ microparticulates in the nickel matrix after a heat treatment of 400°C, producing a more continuous and dense coated composite layer on the Ti-6Al-4V substrate. This phenomenon is responsible for the Ni/Al₂O₃ composite coating with superior surface hardness, providing high corrosion resistance and corrosive wear protection to the Ti-6Al-4V alloy substrate in Hank's solution.

KEY WORDS:

• Coatings
• Corrosion
• Corrosive Wear

ACKNOWLEDGEMENTS

The author thanks the National Science Council of the Republic of China, Taiwan, for financially supporting this research under Contract No. NSC-99-2221-E-231-002.

Review led by Robert Errichello