Combined field ion microscopy and transmission electron microscopy of heavy ion damage in tungsten

Abstract

A field ion microscopy (FIM) and transmission electron microscopy (TEM) investigation of radiation damage in tungsten after heavy ion bombardment has been carried out. Field ion specimens of tungsten were irradiated with 180–230 keV Xe⁺ ions. The irradiation doses were varied between 4 × 10¹¹ and 4 × 10¹² ions/cm². The irradiated specimens were examined in FIM. Experiments combining both TEM and FIM were performed in order to compare the results obtainable by these two methods. The distribution of defects visible by TEM was inhomogeneous. The influence of the imaging field in FIM on the defects visible in TEM is discussed.

Key Words:

• FIM
• TEM
• tungsten
• heavy ion radiation damage
• depleted zone