Synthesis, Characterization, and Cytotoxicity Analysis of a Biodegradable Polyurethane

, , , &
Pages 291-296 | Received 11 Jan 2005, Accepted 09 Nov 2005, Published online: 07 Feb 2007
 

ABSTRACT

A polyester urethane was synthesized for use in a biodegradable scaffold. The polyurethane was synthesized in a two-step process: first, ester diol was synthesized from lactic acid and polyethylene glycol 400 (PEG 400), then it was polymerized with toluene diisocyanate using dibutyl tin dilaurate (DBTDL) as a catalyst to form a polyester urethane. Polyester urethane has tensile strength of 51–59 MPa and elongation at fracture of 369–439%. FTIR and XRD were used to confirm the formation and structure of the polymer. Hydrolytic degradation was studied in different alkali solutions and in saline water. In order to assess the cellular response of this material, cytotoxicity analysis was carried out against the cell line.

Log in via your institution

Log in to Taylor & Francis Online

PDF download + Online access

  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 61.00 Add to cart

Issue Purchase

  • 30 days online access to complete issue
  • Article PDFs can be downloaded
  • Article PDFs can be printed
USD 561.00 Add to cart

* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.