Compression Testing of Ti-6Al-4V in the Temperature Range of 303–873 K

Abstract

Compression testing of Ti-6Al-4V alloy has been carried out at temperatures between 303 K to 873 K. To prevent embrittlement due to atmospheric oxygen and nitrogen, the samples were given a glass coating, which also acts as a lubricant simultaneously. Dynamic Strain Aging was observed to occur in the temperature range of 600 K to 800 K. Below 600 K stresses were high. Warm working has to be done above 800 K but below 1163 K (0.6 T _m where T _m  = 1940 K) which is the recrystallization temperature. Based on these conclusions, warm extrusion has been successfully carried out in the Materials Forming Laboratory of I.I.T., Madras, Chennai, India.

Keywords:

• Compression
• Dynamic strain aging
• Flow properties
• Temperature
• Ti-6Al-4V
• Warm working
• Work hardening