Weld Diffusion Analysis of Forming Bimetallic Components Using Statistical Experimental Methods

, &
Pages 422-430 | Received 29 Jul 2008, Accepted 23 Oct 2008, Published online: 26 Feb 2009
 

Abstract

Bimetallic components made of aluminium alloy and stainless steel can provide the benefits of light weight and excellent wear resistance. Most literature indicates that good bonding of such dissimilar metals can be achieved by friction welding and diffusion welding. However, poor adaptability to component shapes and long processing time limited their applications. If a large amount of deformation is permitted, hot-pressure welding (HPW) and forge welding (FOW) are more efficient for forming arbitrary shapes of bimetallic components. In order to ensure a successful weld, the diffusion of elements between two metals should be analyzed because this is significant for evaluating the effectiveness and weld quality of those solid-state welding processes. The study described in this article describes a diffusion analysis of forming bimetallic components under HPW and FOW processes, which were performed at various welding temperatures T and forming deformation F. 6063 aluminium alloy and AISI 316L stainless steel were selected as the specimen materials. The good-quality bimetallic components were obtained by FOW at T = 450°C and F = 8 mm. Their welds exhibited an average tensile strength of 111.29 MPa. Using scanning electron microscopy as a tool for metallographic analysis, a full 4 µm thick diffusion layer was found in the weld interface. According to the results of the energy-dispersive X-ray spectroscopy and X-ray diffraction analysis, this layer consisted of several intermetallic compounds such as FeAl3, Fe2Al5, Fe3Al, Al5Fe2, Al13Fe4, and AlFe, which achieved the bonding between aluminium and iron elements. Weld discontinuities existed in the diffusion zone of all HPW components that weakened the overall strengths of their welds. The main cause was recognized to be the temperature drop of the materials that interrupted their coalescence during diffusion. Results were interpreted by statistical experimental methods, which made use of the control charts to analyze the central tendency and spread on the tensile strengths of bimetallic welds produced by both HPW and FOW processes and examine their reliability as well. The present study not only demonstrates that the bimetallic components produced by the FOW are superior in quality and comparable to those reported in previous studies, but also confirms that they are more reliable than the HPW.

ACKNOWLEDGMENTS

The authors would like to thank the company and Central Fund of The Hong Kong Polytechnic University (Project # ZW88) for supporting this study.

Log in via your institution

Log in to Taylor & Francis Online

PDF download + Online access

  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 61.00 Add to cart

Issue Purchase

  • 30 days online access to complete issue
  • Article PDFs can be downloaded
  • Article PDFs can be printed
USD 561.00 Add to cart

* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.