Preparation and Evaluation of Mechanical Properties of 6061Al- B₄C_p Composites Produced via Two-Stage Melt Stirring

Abstract

The present work aims at producing 6061Al metal matrix composites reinforced with 5 and 7 wt% of B₄C particulates at temperature of 750°C via melt stirring method involving two step additions. In order to improve wettability and to avoid agglomeration of B₄C particulates, K₂TiF₆ halide salt in the ratio of 0.2 were mixed with B₄C particulates and the mixture were being dropped into the melt batch wise (twice). The prepared composites were characterized by SEM/EDX and X-RD studies. SEM microphotographs revealed homogeneous dispersion of B₄C particulates without agglomeration in 6061Al matrix. Indexing of the XRD peaks confirmed the presence of α-Al, B₄C and minor phases like Al₃Ti and Al₃BC. Presence of Al₃Ti phase as confirmed by XRD and EDX studies is clear indication of Ti compound/layer formed around the B₄C particles. Further, improvements in mechanical properties like hardness, tensile and compression strengths of the 6061Al matrix were obtained in the composites.

Keywords:

• Casting
• Density
• Diffraction
• Interfaces
• Low-temperature
• Micro-hardness
• Microstructure
• Properties
• Reactions
• Reinforcement
• Salt
• Tensile

Disclaimer

As a service to authors and researchers we are providing this version of an accepted manuscript (AM). Copyediting, typesetting, and review of the resulting proofs will be undertaken on this manuscript before final publication of the Version of Record (VoR). During production and pre-press, errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal relate to these versions also.