Abstract
(1-x)BiFe0.75Mn0.25O3-(x)BaTiO3 (x = 0.1, 0.2, 0.3) solid solutions have been prepared utilizing conventional solid state reaction route. Powder XRD study confirmed the structural evolution from rhombohedral to cubic phase with an incorporation of BaTiO3 (BT). Further insight in to microstructure revealed structural bonding using FTIR spectra and reduced grain size and shape along with reduced porosity with an increasing BT content using SEM studies. Maximum polarization of 56 μC/cm2 was observed for x = 0.3. The magnetoelectric coupling coefficient was obtained successfully by straight line fitting of induced polarization vs. magnetic field graph and was found to be 0.83124 μC/cm2/T.