Air and nitrogen glow discharge were used to replace chromic acid pretreatment to deposit copper film on carbon fiber surfaces from an CuSO4‐HCHO electroless system. A greater copper uptake and a more uniformly coated copper film were obtained for plasma‐treated carbon fibers. The adhesion between the copper film and the carbon fibers was also improved. An orthogonal table L9(34) was used to study the effects of discharge pressure, discharge power, time and gas type on the copper uptake. Scanning electron microscopy (SEM), reflection absorption infrared spectroscopy (RAIR) and X‐ray photoelectron spectroscopy (XPS) at different depths were applied to characterize the physical and chemical changes of the surface of the carbon fibers. The results showed that after plasma treatment, the carbon fiber surface became rough and several types of polar oxygen groups, such as carboxylic acid COOH, esters COOC, quinones Ph˭O, etc., were introduced into the carbon fiber surface. A mechanism of plasma treatment effects on copper electroless deposition on the carbon fiber surface is also suggested.
Influence of Plasma Treatment on the Electroless Deposition of Copper on Carbon Fibers
Log in via your institution
Log in to Taylor & Francis Online
Restore content access
Restore content access for purchases made as guestPDF download + Online access
- 48 hours access to article PDF & online version
- Article PDF can be downloaded
- Article PDF can be printed
Issue Purchase
- 30 days online access to complete issue
- Article PDFs can be downloaded
- Article PDFs can be printed
Related Research
People also read lists articles that other readers of this article have read.
Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.
Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.