Synthesis and Characterization of Organosoluble Polyimides Containing Pyridyl Moiety with Ether Linkages

Two novel diamine monomers, bis(4‐amino‐3,5‐dimethylphenyl)‐3‐pyridyl methane and bis(4‐aminophenoxy‐3,5‐dimethylphenyl)‐3‐pyridyl methane were synthesized. A series of pyridine containing aromatic polyimides derived from the diamines were synthesized through a typical two‐step polymerization method. Most of the polymers show good solubility in NMP, DMAc, DMF, DMSO and CHCl₃ at room temperature. These polyimides exhibit T_g in the range of 249–317°C and 10% wt loss (T₁₀) takes place in the range of 474–564°C in N₂ and 469–558°C in air. The polymers have tensile strength in the range of 88–96 MPa, elongation at break in the range of 8.5–12.5% and tensile modulus in the range of 1.5–2.1 GPa. These polyimides also have low dielectric constant (3.26–3.64 at 1 KHz and 3.24–3.61 at 10 KHz) and low moisture absorption (0.42–0.89%).

Keywords:

• polyimides
• diamine
• pyridine moiety
• solubility
• thermal stability