Abstract
Novel copolymers of trisubstituted ethylene monomers, alkyl ring-substituted 2-phenyl-1,1-dicyanoethylenes, RC6H4CH = C(CN)2 (where R is 2-methyl, 3-methyl, 4-methyl, 4-ethyl, 4-i-propyl, 4-butyl, 4-i-butyl, and 4-t-butyl) and 4-fluorostyrene were prepared at equimolar monomer feed composition by solution copolymerization in the presence of a radical initiator (ABCN) at 70°C. The composition of the copolymers was calculated from nitrogen analysis, and the structures were analyzed by IR, 1H and 13C-NMR. The order of relative reactivity (1/r 1) for the monomers is 4-ethyl (42.6) > 4-butyl (29.4) > 4-t-butyl (26.7) > 4-i-butyl (1.6) > 4-i-propyl (1.29) > 3-methyl (1.26) > 2-methyl (0.8) > 4-methyl (0.4). High T g of the copolymers, in comparison with that of poly(4-fluorostyrene) indicates a substantial decrease in chain mobility of the copolymer due to the high dipolar character of the trisubstituted ethylene monomer unit. Decomposition of the copolymers in nitrogen occurred in two steps, first in 183–500°C range with residue (5–30% wt.), which then decomposed in the 500–800°C range.
Acknowledgements
We thank the National Science Foundation Polymer Program (DMR-0710520) for support. We are grateful to acknowledge that the project is partly supported by the Coatings Industry Education Foundation, Chicago Society of Coating Technology and Office of Sponsored Programs and Research of DePaul University.
Notes
a Polymerization time was 24 h.
b T g transition was observed by DSC.