Preparation and Characterization of Quaternized Chitosan Under Microwave Irradiation

Abstract

For the first time, N-(2-hydroxyl) propyl-3-trimethyl ammonium chitosan chloride (HTCC) was prepared through a fast, easy and efficient method with the assistance of microwave irradiation, and the quaternized chitosan was also degraded via the microwave irradiation. A comparative study was performed by using the conventional heating method to prepare HTCC. The structure and property of the quaternized chitosan obtained by these two methods were characterized by GPC, XRD, FTIR, NMR, TG and elemental analysis. It was shown that quaternized chitosan was successfully prepared within 50 min via microwave irradiation method, while a much longer time of 6–7 h was needed with the conventional heating method. The substitutions both occurred on the C2 position of chitosan with the two different methods, and their HTCC products had weight average similar molecular weight (Mw), structure and thermal stability. The HTCC prepared by the microwave irradiation method had a little lower degree of substitution (DS) than those prepared via conventional heating with the same mole ratio (6:1) of the intermediate to chitosan. The degradation study showed that the Mw of HTCC decreased rapidly from 4.6 × 10⁵ to 1.1 × 10⁵ in 1 h under microwave irradiation, while it only decreased from 4.6 × 10⁵ to 2.1 × 10⁵in 1 h through conventional heating degradation. These results revealed that microwave irradiation is a more efficient and environment-friendly way to obtain the water-soluble chitosan derivatives and their degraded products.

Keywords:

• Quaternized chitosan
• microwave irradiation
• conventional heating
• thermal stability

Acknowledgements

The authors wish to express their gratitude for the financial support from National Key Basic Research Program (973 Program) of China (No: 2010CB732201), the National Natural Science Foundation of China (No. 30972323), the Fundamental Research Funds for the Central Universities, SCUT (No.2009ZM0182), United Opening Foundations of Marine Biology Key Laboratory of Chinese Academy of Sciences/Guangdong Province (LMB081002).