Novel Copolymers of Styrene. 15. Phenoxy Ring-Substituted Methyl 2-Cyano-3-Phenyl-2-Propenoates

Abstract

Electrophilic trisubstituted ethylenes, phenoxy ring-substituted methyl 2-cyano-3-phenyl-2-propenoates, RPhCH=C(CN)CO₂CH₃, where R is 4-(4-BrC₆H₅O), 2-(4-ClC₆H₅O), 3-(4-ClC₆H₅O), 4-(3-ClC₆H₅O), 4-(4-ClC₆H₅O), 4-(4-FC₆H₅O), 2-(3-CH₃OC₆H₅O), 2-(4-CH₃OC₆H₅O), 3-(4-CH₃OC₆H₅O), 4-(4-CH₃OC₆H₅O), 3-(4-CH₃C₆H₅O) were prepared and copolymerized with styrene. The monomers were synthesized by the piperidine catalyzed Knoevenagel condensation of phenoxy ring-substituted benzaldehydes and methyl cyanoacetate, and characterized by CHN analysis, IR, ¹H and ¹³C-NMR. All the ethylenes were copolymerized with styrene (M₁) in solution with radical initiation (ABCN) at 70°C. The compositions of the copolymers were calculated from nitrogen analysis and the structures were analyzed by IR, ¹H and ¹³C-NMR. The order of relative reactivity (1/r₁) for the monomers is 4-(4-CH₃OC₆H₅O) (6.07) > 3-(4-ClC₆H₅O) (3.38) > 3-(4-CH₃OC₆H₅O) (2.78) > 4-(3-ClC₆H₅O) (2.77) > 2-(4-ClC₆H₅O) (2.29) > 3-(4-CH₃C₆H₅O) (1.98) > 4-(4-FC₆H₅O) (1.92) > 4-(4-ClC₆H₅O) (1.89) > 2-(3-CH₃OC₆H₅O) (1.39) > 2-(4-CH₃OC₆H₅O) (0.90) > 4-(4-BrC₆H₅O) (0.77). Relatively high T_g of the copolymers in comparison with that of polystyrene indicates a decrease in chain mobility of the copolymer due to the high dipolar character of the trisubstituted ethylene monomer unit. Decomposition of the copolymers in nitrogen occurred in two steps, first in the 200-500°C range with residue (2.5-8.0% wt), which then decomposed in the 500-800°C range.

Keywords:

• Trisubstituted ethylenes
• radical copolymerization
• styrene copolymers