On the Action of γ Radiation on Solid C₆₀ and C₇₀ Fullerenes: A Comparison with Graphite Irradiation

Abstract

C₆₀ and C₇₀ fullerene have been treated in sealed flasks under Ar with γ radiation using radiation dosages ranging from 10 to 1000 kGy. The treated samples studied by electronic and FT-IR spectroscopy have not shown any evidence about fullerenes decomposition or radiopolymerization. However, through Raman spectroscopy it was possible to observe that γ radiation induces C₆₀ dimerization and trimerization. It has additionally been discovered that γ-treated C₆₀ (oligomerized) can be easily photopolymerized in the solid state by post-irradiation with laser light at 514 nm while this phenomenon has not been observed by using laser light at 782 nm and considerably higher laser power. Previously to this study, C₆₀ photopolymerization was known to occur only by using ultraviolet light.

For comparison also graphite was irradiated with 1000 kGy of γ radiation. Irradiated graphite shows considerably changes in its Raman spectrum, showing the formation of glassy carbon domains, perhaps carbon onions. The l_d bandshift to 1310 cm⁻¹ could be interpreted in terms of formation of hexagonal diamond.