Multiferroic and magnetoelectric properties of MnFe₂O₄/(Pb_0.8Sr_0.2)TiO₃ composite films

Abstract

MnFe₂O₄/(Pb_0.8Sr_0.2)TiO₃ (MFO/PST20) heterostructured composite films with three different structures have been grown on Pt/TiO₂/SiO₂/Si substrates by metal–organic decomposition processing via spin coating technique. The structural analysis revealed that the crystal axes of the MnFe₂O₄ are aligned with those of the PST20 ferroelectric matrix with obvious interfaces and no diffusions exist in all the three composite films. These composite films exhibit simultaneously multiferroic and magnetoelectric responses at room temperature. The growth structure of MFO and PST20 layers has an effect on multiferroic and magnetoelectric coupling behaviours of the composite films. The bi- and four-layered MFO/PST20 composite films exhibit superior ferroelectric properties compared to the tri-layered film. The increasing MFO and PST20 layers in the composite films enhance ferromagnetic properties and are closely related to the strain release in MnFe₂O₄ phase. The MFO/PST20 bi-layered composite film shows a high magnetoelectric voltage co-efficient α_E ~ 194 mVcm⁻¹Oe⁻¹ at a dc magnetic field H_dc ~ 2.5 kOe. A significant decrease in α_E value has been observed for tri- and four- layered composite films. A close correlation between phase selective residual stress and magnetoelectric properties has been emerged. The results are reasonably encouraging for employing MnFe₂O₄ for growing multiferroic–magnetoelectric composite films.

Keywords:

• Composite films
• multiferroic properties
• magnetoelectric coupling effect
• conduction mechanism

Acknowledgement

The authors NSN and Kanchan Bala wish to acknowledge Department of Science and Technology (DST), New Delhi, India for providing financial support to carry out this work [grant number SR/S2/CMP-0101/2010(G)].

Disclosure statement

No potential conflict of interest was reported by the authors.