Abstract
A 3D dislocation dynamics study to ascertain the probable path of stage-I fatigue crack propagation across the persistent slip band (PSB) in austenitic stainless steel is presented. Cyclic plasticity and the resulting crack tip slip displacement (CTSD) are evaluated for cracks of varying length introduced at PSB-center and at two PSB-matrix interfaces. CTSD attains high value at either of the two interfaces irrespective of the proximity of crack front to the grain boundary. Further, a difference in microcrack propagation rate is also observed among the two interfaces. The present results assert microcrack propagation preferrentially along one of the two PSB-matrix interfaces rather than at the PSB-center. A pre-existing PSB dislocation structure localises the cyclic slip for crack lengths up to approximately half of the grain depth for an applied strain range of 2 × 10−4.