Extrinsic plastic hardening of polymer thin films in flat punch indentation

ABSTRACT

Confined geometries offer useful and experimentally amenable mechanical testing arrangements in which to study the molecular and micro-structural processes which govern plastic yield in stress environments dominated by hydrostatic pressure over shear. However, the changes to macroscopic stress – strain behaviour that result from switching from an unconfined mode such as uniaxial compression to a confined one are often overlooked and display a surprising level of complexity, even for simple elastic – plastic constitutive models. Here we report a confinement induced strain hardening effect in polystyrene thin films achieved through repeated plastic loading with a cylindrical flat punch whose diameter is many times the initial film thickness. This high aspect ratio combines with constraint provided by film material surrounding the contact to generate a state of confined uniaxial strain in the indented region, rendering the deformation one dimensional. By repeated loading past the yield point into the plastic domain, we achieve a 66% increase in the confined yield stress, from 0.3 GPa to 0.5 GPa. Through finite element simulation and analytic modelling of the principal stresses and strains, we show that this effect arises not from intrinsic changes to the structure of the material, but rather residual stresses imparted during plastic loading. We contrast this effect with intrinsic changes to glassy thin films such as physical ageing and thermal cross-linking.

KEYWORDS:

• Thin-film mechanics
• indentation
• plastic deformation
• amorphous solids
• disordered materials

Acknowledgements

OB and GLWC acknowledge support from Science Foundation Ireland grants SFI/AMBER/12/RC/2278 and 08/IN.1/I1932.

Disclosure statement

No potential conflict of interest was reported by the author(s).

Additional information

Funding

This work was supported by Science Foundation Ireland [grant numbers SFI/AMBER/12/RC/2278, 08/IN.1/I1932].