Influence of different surface treatments on zirconia/resin shear bond strength using one-bottle universal adhesive

ABSTRACT

This study was designed to evaluate the effect of different treatments on the zirconia/resin shear bond strength (SBS) using commercial one-bottle universal adhesive. Zirconia discs with different surface treatments (blank control; airborne-particle-abrasion; glazing) were bonded to the bovine enamel surfaces using one-bottle universal adhesive. All specimens were tested for SBS (MPa) before and after 10000 thermocycles. Statistically analysis were conducted by using one-way analysis of variance and multiple-comparison least significant difference tests (α = 0.05). Airborne-particle-abrasion group showed higher SBS (36.19 ± 11.86) than control group (14.98 ± 5.90) and glazing group (10.63 ± 5.39) (p < 0.05). After thermocycling test, the SBS significantly decreased for control group (8.84 ± 2.55) and glazing group (6.18 ± 2.78) while not for airborne-particle-abrasion group (41.5 ± 7.95). One-bottle universal adhesives combined with airborne-particle-abrasion showed quite high SBS of zirconia/resin, which was appropriate for bonding of zirconia restoration.

KEYWORDS:

• Zirconia
• adhesion
• shear bond strength
• surface treatments
• one-bottle universal adhesive

Disclosure statement

No potential conflict of interest was reported by the authors.

Additional information

Funding

This study was supported by grants from the Natural Science Foundation of China [project no. 51772007 and 50872003].