Nanoindentation and scratch behaviour of Ni–P electroless coatings

ABSTRACT

In the present paper, the mechanical properties and the scratch failure mechanisms of Ni–P electroless coatings are described. The material microstructure was studied in as-deposited and annealed conditions through SEM and EDS analyses. Nanoindentation measurements on the coatings showed a remarkable hardening due to the crystallization and precipitation behaviour produced by annealing. The scratch tests, conducted by increasing the load during scratch, revealed the coating failure mechanisms in a broad range of applied stresses up to delamination.

KEYWORDS:

• Ni–P coatings
• electroless
• nanoindentation
• cyclic loading
• scratch
• scanning electron microscopy
• damage