ABSTRACT
Designed and synthesized a series of imidazolium-functionalized Poly (2, 6-dimethyl-1, 4-phenylene oxide) (Im-PPO) containing pendant imidazole groups, which were used to supply functional sites for acid–base interaction with the doping phosphoric acid. The imidazolium-functionalized Poly (2, 6-dimethyl-1, 4-phenylene oxide) membranes obtained by the solution-casting method were doped with phosphoric acid (PA). The PA content, swelling, and tensile strength of the different membranes doped with PA were measured. With the increase of the length of side chains on the imidazole groups, the membrane showed different properties. The proton conductivity at a level of 3.7 × 10−2 S/cm was achieved at 160°C by the MeIm-PPO imidazolium composite membrane.
Graphical abstract
![](/cms/asset/7bf9f62b-73bf-4b5f-b107-1bb85b0d00c5/lpte_a_1750650_uf0001_b.gif)
Additional information
Notes on contributors
Shanshan Wang
Shanshan Wang:Master, assistant experimenter of Beijing Institute of Technology, mainly engaged in large-scale equipment management, experimental teaching, test method development and membrane material research.
Qifeng Li
Qifeng Li:Master's degree, graduated from Beijing University of Chemical Technology, mainly engaged in the research of high temperature proton exchange membrane fuel cells.
Fanghui Wang
Fanghui Wang:Associate Professor of Beijing University of Chemical Technology, mainly engaged in the research of key materials for fuel cells and hydrogen production catalysts.