Several poly(aryl ether)s have been prepared by the condensation of 1,3‐bis(4‐hydroxy phenyl) benzene with different trifluoromethyl activated bis‐fluoro compounds. IR, 1H and 13C NMR, and elemental analyses have established the resulting polymer structures. The properties of the polymers have been evaluated by DSC, TGA, dynamic mechanical analysis (DMA) and stress–strain analysis. The polymers 1a and 1c showed semi‐crystalline behavior as evident by sharp crystalline melting peaks at 299°C and 330°C along with glass transitions at 202°C and 216°C, respectively. The polymers showed very good thermal stability in air, high modulus, and high tensile strength with low elongation at break.