Abstract
The experiments in this paper were performed to research the mechanism of cobalt cementation from high cobalt zinc sulphate solution by zinc dust. The reduction potential of zinc during cementation was determined to investigate the morphology of products. Residues after the cementation process from zinc sulphate solution were analyzed by SEM and EPMA to investigate the morphology of products. Different temperature will cause different structure of particles. The reaction mechanism of cobalt removal by zinc dust is thought to be as follows: first, the Co2+ forms Co–Zn alloy with zinc particles, and the reaction reaches equilibrium quickly; second, the Co–Zn alloy continues reacting to Co with Co2+, which is the control process of the whole reaction.
Abstract
Les expériences présentées dans cet article ont été réalisées pour étudier le mécanisme de cémentation du cobalt depuis une solution de sulphate de zinc a haute teneur en cobalt par de la poussière de zinc. Le potentiel de réduction du zinc pendant la cémentation a été déterminée pour étudier la morphologie des produits. Les résidus du processus de cémentation de la solution de sulphate de zinc ont été analysés par SEM et EPMA pour étudier la morphologie des produits. Des températures differentes causent des structures de particule différentes. Le mécanisme de réaction de dépose du cobalt par la poussière de zinc est considéree de la manière suivante : premièrement, le Co2+ forme un alliage Co‐Zn avec les particules de zinc, et la réaction atteint l’équilibre rapidement ; deuxièmement, l’alliage Co‐Zn continue a réagir avec le Co2+ pour former du Co, qui est le processus de contrôle de toute la réaction.